Oxidation behaviors of Fe-25Cr-20Ni-χNb austenitic weld metals at 1100 °C in ambient air: Role of elemental niobium
发布时间：2019-10-09点击次数：
- 影响因子：7.4
- DOI码：10.1016/j.corsci.2019.108137
- 所属单位：中国科学院金属研究所
- 教研室：0
- 发表刊物：Corrosion Science
- 刊物所在地：英国
- 项目来源：中国科学院重点研究计划
- 关键字：A. Austenitic weld metal; B. SEM; B. XRD; C. High temperature corrosion; C. Oxidation
- 摘要：The isothermal oxidation behaviors of the Fe-25Cr-20Ni-χNb (0–1.6 wt.%) weld metals have been investigated in air at 1100 °C. Results showed that niobium has a detrimental effect on the elevated temperature oxidation resistance of the chromia-forming weld metals. In the Nb content range studied, the Nb content of 1.6 wt.% showed the most deleterious effect on the chromia layer. Niobium promoted the chromium depletion underneath the oxide/matrix interface by impeding the chromium diffusion, which ruined the compactness of the chromia layer. The oxidation of niobium at the oxide layer/metal interface can further cause severe damage to the chromia layer, resulting in catastrophic oxide spallation.
- 备注：0
- 论文类型：研究论文
- 论文编号：108137
- 学科门类：工学
- 卷号：159
- 是否译文：否
- 发表时间：2019-01-01
+